REKAYASA PEMBUATAN MEMBRAN SELULOSA ASETAT UNTUK PEMISAHAN LARUTAN DETERJEN
Article Sidebar
Main Article Content
Abstract
Acetic cellulose membrane is made from acetic cellulose, formamide and acetone using variations of composition and condition. Flux and rejection value was influenced by the characteristic of the composition and thickness membrane, pressure and time of operation. The result showed that flux would decrease and the rejection would increase if the composition of the acetic cellulose too much, while the thickness didn’t influence rejection score, but decreased the flux. The optimum pressure of operation to obtain the hight flux and rejection on their process was 1,75 bar for membrane compotition 14,8% (w/w) of acetic cellulose and the thickness 0,083 mm for membrane with operation time 75 minute. The optimum result was flux permeate 432,92 L/m2 days and 93,09% rejection score.
Downloads
Article Details
Pengiriman manuskrip ke Jurnal Purifikasi diartikan bahwa karya tersebut belum pernah dipublikasikan pada jurnal lain serta tidak dalam pertimbangan untuk dipublikasikan di tempat lain. Penulis dengan ini bersedia menyerahkan hak cipta manuskrip beserta isinya kepada Jurnal Purifikasi, jika diterima untuk publikasi. Manuskrip yang diterima akan dipublikasikan dalam bentuk cetak dimana ISSN terikat dalam bentuk cetak bukan dalam bentuk online (pdf). Penulis tidak diperbolehkan mempublikasikan karyanya ke dalam bentuk lain (jurnal) tanpa seizin pengelola Jurnal Purifikasi.
Dengan menyerahkan manuskrip, penulis telah dianggap mengetahui segala hak dan kewajiban yang melekat pada setiap manuskrip.