SOLIDIFIKASI DAN STABILISASI BAHAN BUANGAN KERAK BAJA DARI INDUSTRI BAJA MALAYSIA
Article Sidebar
Main Article Content
Abstract
The study was conducted to test steel’s slag wasted from Malaysia’s steel industry as concrete using solidification/ stabilization method (S/S). The concrete was tested using pressurized test and Toxicity Characteristic Leaching Procedure (TCLP). Ions that were tested were Cd, Cu, Cr3+, Cr6+, Fe, Pb, Mn, S, Zn and Ni. After TCLP procedure, all ion concentration were under threshold limit issued by the Jabatan Alam Sekitar (JAS) standard. Ion concentration Al, Cu, Cr6+, Fe, Mn and Ni were increased along with curing age. Meanwhile, Cd and Pb ions were decreased along with curing age. Based on compressive test, mortar that contain steel slag were more stronger than control mortar in every curing age. This research concluded that steel slag in Malaysia’s industrial steel could be used as alternative building material.
Downloads
Article Details
Pengiriman manuskrip ke Jurnal Purifikasi diartikan bahwa karya tersebut belum pernah dipublikasikan pada jurnal lain serta tidak dalam pertimbangan untuk dipublikasikan di tempat lain. Penulis dengan ini bersedia menyerahkan hak cipta manuskrip beserta isinya kepada Jurnal Purifikasi, jika diterima untuk publikasi. Manuskrip yang diterima akan dipublikasikan dalam bentuk cetak dimana ISSN terikat dalam bentuk cetak bukan dalam bentuk online (pdf). Penulis tidak diperbolehkan mempublikasikan karyanya ke dalam bentuk lain (jurnal) tanpa seizin pengelola Jurnal Purifikasi.
Dengan menyerahkan manuskrip, penulis telah dianggap mengetahui segala hak dan kewajiban yang melekat pada setiap manuskrip.